LSQ004.43-Z.JZ42-CQT10.2-(#8-18)-L1.25in-Q-EZna-T4 |
Tapping screws-Building.ASME IND HWH TYPE B |
Z.JZ42 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#8-18) | - | 1.25in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.18-Z.JZ18-CQT10.2-(#8-18)-L3.75in-B-EZne-T4 |
Tapping screws-Building.ASME IND HWH SLT TYPE B |
Z.JZ18 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#8-18) | - | 3.75in | Partially Threaded | Zn-Plating Blue 5-10μm Passivation,72h | SWRCH22A |
|
|
LSQ004.35-Z.JZ35-CQT10.2-(#8-18)-L0.375in-Q-EZna-T4 |
Tapping screws-Building.ASME SERRATED HWH TYPE AB |
Z.JZ35 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#8-18) | - | 0.375in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.53-Z.JZ53-CQT13-(#10-8)-L2.5in-B-EZna-T2 |
Tapping screws-Building.ASME Flat head TROX Type 17 |
Z.JZ53 | CARBURIZING CASE HARDEN MIN0.10mm DEEP; Surface Hardness 450-720HV0.3 | (#10-8) | - | 2.5in | Partially Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.53-Z.JZ53-CQT13-(#10-8)-L3.5in-B-EZna-T2 |
Tapping screws-Building.ASME Flat head TROX Type 17 |
Z.JZ53 | CARBURIZING CASE HARDEN MIN0.10mm DEEP; Surface Hardness 450-720HV0.3 | (#10-8) | - | 3.5in | Partially Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.46-Z.JZ46-CQT10.3-D6.0X2.7-L50-B-MGLa-T4 |
Tapping screws-Building.ASME IND HWH HD with full shank Plastic thread screw flat end |
Z.JZ46 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.13-0.28mm,Core Hardness 28-36HRC | D6.0X2.7 | - | 50 | Partially Threaded | MAGNI,12μm,Silver,240h no white rust,840h no red rust | 10B21 |
|
|
LSQ004.54-Z.JZ54-CQT11.2-(#9-14)-L2.5in-Q-EZna-T2-ZXD |
Tapping screws-Building.ASME IND HWH W/SHOULD TYPE 17 |
Z.JZ54 | CARBURIZING CASE HARDEN ; Surface Hardness 53-62HRC;Depth 0.10-0.23mm,Core Hardness 28-38HRC | (#9-14) | - | 2.5in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.48-Z.JZ48-CQT10.1-(#4-24)-L19-Q-EZnBLa-T4 |
Tapping screws-Building.ASME Pan Head TORX TYPE AB |
Z.JZ48 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.05-0.18mm,Core Hardness 28-36HRC | (#4-24) | - | 19 | Fully Threaded | Zn-Plating Black,480h no red rust | SAE1022 |
|
|
LSQ004.49-Z.JZ49-CQT10.2-(#8-18)-L50-Q-EZnBLa-T4 |
Tapping screws-Building.ASME Flat Head TORX TYPE AB |
Z.JZ49 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#8-18) | - | 50 | Fully Threaded | Zn-Plating Black,480h no red rust | SAE1022 |
|
|
LSQ004.50-Z.JZ50-CQT10.2-D3.0X1.34-L19-B-MGLB-T4 |
Tapping screws-Building.ASME IND HWH HD Plastic thread screw flat end |
Z.JZ50 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | D3.0X1.34 | - | 19 | Partially Threaded | MAGNI,12μm,Grey,240h no white rust,840h no red rust | SAE1022 |
|
|
LSQ004.42-Z.JZ43-CQT10.2-(#10-16)-L1in-Q-LXB-T4 |
Tapping screws-Building.ASME IND HWH SLT TYPE AB |
Z.JZ43 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#10-16) | - | 1in | Fully Threaded | RUSPERT,1000h | A307 |
|
|
LSQ004.41-Z.JZ39-CQT10.2-#6-L0.625in-Q-EZna-T4 |
Tapping screws-Building.ASME Pan PH TYPE B |
Z.JZ39 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | #6 | - | 0.625in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.42-Z.JZ43-CQT10.2-#8-L0.375in-Q-EZna-T4 |
Tapping screws-Building.ASME IND HWH SLT TYPE AB |
Z.JZ43 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | #8 | - | 0.375in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.09-Z.JZ02-CQT11.2-(#7-23)-L0.4375in-Q-P-T1 |
Tapping screws-Building.ASME Pan Framing Head Serration Phillips sharp |
Z.JZ02 | CARBURIZING CASE HARDEN ; Surface Hardness 53-62HRC;Depth 0.10-0.23mm,Core Hardness 28-38HRC | (#7-23) | - | 0.4375in | Fully Threaded | Phosphating,Black | - |
|
|
LSQ004.36-Z.JZ36-CQT10.2-#8-L0.375in-Q-EZna-T4 |
Tapping screws-Building.ASME HWH W/NIBS SLT TYPE AB |
Z.JZ36 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | #8 | - | 0.375in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.21-Z.JZ21-CQT10.2-(#10-16)-L0.75in-Q-EZna-T4 |
Tapping screws-Building.ASME IND HWH W/NIBS SLT TYPE AB |
Z.JZ21 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#10-16) | - | 0.75in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.34-Z.JZ34-CQT10.2-(#8-18)-L0.625in-Q-EZna-T4 |
Tapping screws-Building.ASME SERRATED HWH PH TYPE AB |
Z.JZ34 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#8-18) | - | 0.625in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.34-Z.JZ34-CQT10.2-(#8-18)-L0.375in-Q-EZna-T4 |
Tapping screws-Building.ASME SERRATED HWH PH TYPE AB |
Z.JZ34 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#8-18) | - | 0.375in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.06-Z.JZ16-CQT10.2-(#8-18)-L0.5in-Q-EZna-T4 |
Tapping screws-Building.ASME IND HWH W/SHOULD SLT |
Z.JZ16 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#8-18) | - | 0.5in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|
|
LSQ004.27-Z.JZ27-CQT10.2-(#8-18)-L0.625in-Q-EZna-T4 |
Tapping screws-Building.ASME HWH W/SHOULD SLT TYPE AB |
Z.JZ27 | CARBURIZING CASE HARDEN ; Surface Hardness 45-53HRC;Depth 0.10-0.23mm,Core Hardness 28-36HRC | (#8-18) | - | 0.625in | Fully Threaded | Zn-Plating Blue 48h | SWRCH22A |
|